Depth of cure, mechanical properties and morphology of dual-cure bulk-Fill composites / Profundidad de curado, propiedades mecánicas y morfología de resinas compuestas duales

This study evaluated selected structural and physical properties, such as degree of conversion (DC), Vickers hardness (VHN), and compression strength (CS), of three new dual-cure bulk-fill resin-based composites (RBCs; ACTIVA, HyperFIL, and Fill-Up) and compared them to those of a conventional RBC (Filtek Z250) at three clinically relevant depths. Samples (n=180) were prepared in three depths (2,4, and 6mm). Fourier-transform infrared spectroscopy (FTIR) analysis and VHN and CS tests were performed. The DC value was calculated by considering the relative change in the aliphatic C=C peaks. The fractured surfaces of representative samples were characterized using scanning electron microscopy (SEM). Data were statistically evaluated using two-way analysis of variance and post hoc Bonferroni tests (p<0.05). According to the VHN results, Filtek Z250 showed the highest bottom/top hardness ratio (97.94±1.01) at 2mm thickness and ACTIVA showed the lowest bottom/top hardness ratio (43.48±5.64) at 6mm thickness (p<0.001). According to the FTIR results, the DC decreased with increasing thickness in all materials (p<0.05). Filtek Z250 showed the highest (301±12.4 MPa) and ACTIVA exhibited the lowest (232±17.2 MPa) CS values at 2mm thickness (p<0.05). The lowest CS values were obtained for ACTIVA, and the highest values were obtained for Filtek Z250 for samples with thicknesses of 4 and 6mm, respectively (p<0.05). The structural features of restorative composites, such as the resin chemistry and filler type and content, and the operational parameters (i.e., material thickness and curing conditions) strongly affect crosslinking reactions and thus the DC, VHN, and CS values.

Este estudio evaluó propiedades físicas y estructurales, como el grado de conversión (DC), la dureza Vickers (VHN) y la resistencia a la compresión (CS), de tres nuevos compósitos a base de resina de curado dual tipo bulk (RBC; ACTIVA , HyperFIL y Fill-Up) y los comparó con los de una resina compuesta convencional (Filtek Z250) en tres profundidades clínicamente relevantes. Se prepararon muestras (n=180) en tres profundidades (2,4 y 6mm). Se realizaron análisis de espectroscopia infrarroja por transformada de Fourier (FTIR) y pruebas VHN y CS. El valor de DC se calculó considerando el cambio relativo en los picos alifáticos C=C. Las superficies fracturadas de muestras representativas se caracterizaron mediante microscopía electrónica de barrido (MEB). Los datos se evaluaron estadísticamente mediante análisis de varianza de dos vías y pruebas post hoc de Bonferroni (p<0,05). De acuerdo con los resultados de VHN, Filtek Z250 mostró la relación de dureza inferior/superior más alta (97,94±1,01) con un espesor de 2mm y ACTIVA mostró la relación de dureza inferior/superior más baja (43,48±5,64) con un espesor de 6mm (p<0,001). De acuerdo con los resultados de FTIR, la DC disminuyó al aumentar el espesor en todos los materiales (p<0,05). Filtek Z250 mostró los valores de CS más altos (301±12,4 MPa) y ACTIVA los más bajos (232±17,2 MPa) a 2mm de espesor (p<0,05). Los valores más bajos de CS se obtuvieron para ACTIVA y los valores más altos para Filtek Z250 para muestras con espesores de 4 y 6mm, respectivamente (p<0,05). Las características estructurales de las resinas compuestas de restauración, como la química; además del tipo y contenido del relleno, y los parámetros operativos (es decir, el espesor del material y las condiciones de curado) afectan en gran medida las reacciones de interacción química y, por lo tanto, los valores de DC, VHN y CS.

Influence of etching Mode and composite type on bond strength to biodentine using a ''No-Wait'' universal adhesive / Influencia del modo de grabado y del tipo de resina en la resistencia adhesiva al Biodentine utilizando un adhesivo universal tipo "no-wait"

Abstract: The purpose of this study was to compare the shear bond strength (SBS) of four resin-based composite materials to a silicate-based cement using a ''no-wait'' universal bond with self-etch (SE) and etch-and-rinse (ER) modes. Acrylic blocks (n=80, 2mm depth, 5mm diameter central hole) were prepared. The holes were filled with BiodentineTM (BD) and divided into 4 main groups (n=20) according to the composite resin type used: Group FZ250: FiltekTM Z250 Universal Restorative (microhybrid), Group SDR: SDR Plus U Bulk Fill Flowable (low-viscosity bulk-fill), Group FBP: FiltekTM Bulk Fill Posterior (high-viscosity bulk-fill), Group EF: EsFlow™ Universal Flowable Composite (nanohybrid). A 'no-wait' universal bond (Clearfil Universal Bond Quick) was used for bonding application. Then each group was divided into 2 subgroups according to the etching mode applied (ER and SE). SBSs were measured and stereomicroscope was used to identify the failure modes. Selected samples of fracture surfaces were imaged by SEM. Tukey's post-hoc and One-way ANOVA tests were used to analyze data. There were statistically significant differences among the composite groups (p 0.05). The SBS of BD to the resin composites depends on the composite type but application of the 'no-wait' universal bond in different etching modes is regardless of the SBS of BD to resin composites.

Resumen El objetivo de este estudio fue comparar la resistencia de adhesión al cizallamiento (SBS) de cuatro resinas con un cemento a base de silicato utilizando una adhesivo universal "no-wait" de autograbado (SE) y grabado y lavado (ER). Se prepararon bloques acrílicos (n=80, de 2mm de profundidad y un agujero central de 5mm de diámetro). Los agujeros se rellenaron con BiodentineTM (BD) y se dividieron en 4 grupos principales (n=20) según el tipo de resina compuesta utilizada: Grupo FZ250: FiltekTM Z250 Universal Restorative (microhíbrido), Grupo SDR: SDR Plus U Bulk Fill Flowable (bulk-fill de baja viscosidad), Grupo FBP: FiltekTM Bulk Fill Posterior (bulk-fill de alta viscosidad), Grupo EF: EsFlow™ Universal Flowable Composite (nanohíbrido). Para la aplicación de la adhesión se utilizó un adhesivo universal "no-wait" (Clearfil Universal Bond Quick). A continuación, cada grupo se dividió en 2 subgrupos según el modo de grabado aplicado (ER y SE). Se midieron los SBS y se utilizó el estereomicroscopio para identificar los modos de fallo. Las muestras seleccionadas de las superficies de fractura se analizaron mediante SEM. Se utilizaron las pruebas post-hoc de Tukey y ANOVA de una vía para analizar los datos. Hubo diferencias estadísticamente significativas entre los grupos de composites (p0,05). La SBS de la BD a los composites de resina depende del tipo de composite, pero la aplicación de la unión universal "no-wait" en los diferentes modos de grabado es independiente de la SBS de la BD a los composites de resina.

Knowledge, stress levels, and clinical practice modifications of Turkish dentists due to COVID-19: a survey study

Abstract: Dentists are exposed to the highest risk of occupational respiratory and droplet infections by working face-to-face with patients. The aim of this study was to investigate the knowledge of symptoms and modes of transmission of COVID-19, stress levels and clinical practice modifications of Turkish dentists during the COVID-19 pandemic. An online survey (15 questions) was sent to Turkish dentists from May 5 to 12 May, 2020. The survey comprised questions about dentists' demographic characteristics, their knowledge about COVID-19, stress levels and the measures taken in dental clinics against COVID-19. This study included a total of 1,095 Turkish dentists. The data were expressed as frequency with percentage values for overall variables. Dentists were most familiar with high fever among the symptoms of COVID-19 (99.4%) and 99.2% of them reported that COVID-19 was transmitted with eye, mouth and nasal mucosa contact on surfaces contaminated with the droplets of infected persons. While the stress levels of females were higher than males, the stress levels of dentists with more than 20 years of professional experience were found to be lower. Regarding the precautions to be taken as a preventive measure when working again, 86.6% of the dentists took precautions by increasing daily patient care intervals and only 38.4% of the dentists wore an N95 mask. During this pandemic, knowing the conditions about when the treatments can be applied and the precautions to be taken will shed light on dentistry staff. Current recommendations of national authorities about the coronavirus should be followed.